Marine Engine Heat Treatment Forging Hydraulic Cylinder Pull Rod 20000mm Length
Products reference:
| Material | 50Mn,25Cr2Ni4MoV,34CrNiMo6,SUS316L,35# |
| Max length | 20000MM |
| Application |
Marine engine,diesel engine pull rod,connect to oil cylinder transmision function |
| Melting process | EF+LF+VD |
| Production process |
Forging+heat treatment+rough machining+finish machining |
| Forging ratio |
≥3.5 |
| Applicable standard | ASTM,ASME,DIN,JIS,ISO,BS,API,EN |
| Executive standard | JB/GB/EN/DIN/JIS/ASME/ASTM/ISO |
|
Certification authority |
ABS,DNV,BV,GL,KR,CCS,LR,NK,RINA,RS |
| Delivery term |
Rough machining(N+T);finish machining(Q+T) |
|
Test equipment |
Spectrograph,UT device,tensile and compact test machine,metalloscope,outside micrometer,bore dial indicator,hardness test machine |
| service | Our service included the forging, process, heat treatment, finish machining, package, local logistics, customers clearance and maritime transport. We took the customer’s requirements as the principal thing, and pay attention on the products quality. |
Custom properties
|
Material elements |
C | Si | Mn | P | S | Cr | Ni | Mo | V |
| 50Mn | 0.48-0.56 | 0.17-0.37 | 0.70-1.00 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | -- | - |
| 35# | 0.32-0.39 | 0.17-0.37 | 0.50-0.80 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | ||
| 25Cr2Ni4MoV | ≤0.25 | ≤0.23 | ≤0.53 | ≤0.006 | ≤0.004 | ≥1.62 | ≥3.75 | ≥0.33 | ≥0.09 |
| 34CrNiMo6 | 0.30-0.38 | ≤0.040 | 0.50-0.80 | ≤0.035 | ≤0.035 | 1.30-1.70 | 1.30-1.70 | 0.15-0.30 | |
| 316L | 0.030 | 1.00 | 2.00 | 0.045 | 0.030 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 |
|
Mechanical property |
Dia.(mm) |
TS/Rm(Mpa) |
YS/Rp0.2(Mpa) |
EL/A5(%) |
RA/Z(%) |
Type Of notch |
Impact energy |
HBW |
| 50Mn | Ø25 | ≥645 | ≥390 | ≥13 | ≥40 | V | ≥31 | ≤255HBS |
| 35# | Ø25 | ≥530 | ≥315 | ≥20 | ≥45 | V | ≥55 | ≤197HBS |
| 34CrNiMo6 | Ø15 | 750-900 | 450-600 | ≥13 | ≥55 | V | -40℃≥20 | ≤269HBS |
| 316L | Ø15 | ≥485 | ≥170 | ≥30 | ≥40 | ≤187HBS |
Process procedure:
Forging process flow quality control: Raw material steel ingot into warehouse(test the chemical content) → Cutting→ Heating(Furnace temperture test) → Heat treatment after forging(Furnace temperture test) Discharge the furnace(blank inspection)→ Machining→ Inspection(UT,MT,Visal diamention, hardness)→ QT→ Inspection(UT, mechanical properties, hardness, grain size)→ Finish machining→ Inspection (dimension)→ Packing and Marking(steel stamp, mark)→ Storage Shipment
Commerce clause
| MOQ | 1PC |
| Delivery time | 30-60 days |
| Package | Wood pallet,steel frame |
| Delivery term | FOB;CIF;CFR；DDU； |
| Payment term | T/T,LC |
| Type of shipping |
By ocean,air |
Keywords:
Pull rod shaft ship inspection forging,marine forging product,classification society of diesel engine pull rod,can be approved by big ten classification society
Người liên hệ: Mr. Arnold
Tel: +86-15-15-15-81-878
Fax: 86-512-58360318
| Văn phòng bán hàng:A 509,HuaJian Mansion,Zhangjiagang City,JiangSu Province,China | |
| +86--13914905080 | |
| arnoldxue@163.com | |