Forging equipment: | 8000T open die hydropess | Melting process: | EF+LF+VD |
---|---|---|---|
Application: | Machinery parts | Forging ratio: | ≥3.5 |
Size: | As drawing | Material: | Steel |
Điểm nổi bật: | roll forging,rolling forging |
8000T Open Die Hydropess Forged Steel Rolls Solid Cold Roller Forging
Products:
finished roller,solid forging roller,cold roller shaft,high speed cold roller,wear resisting cold roller,high Cr cold roller
Products reference:
Material | 4140,60CrMo,9Cr2Mo,90Cr3 |
Forging equipment | 8000t Open die hydropress |
Application |
Cold roller is mainly used for finishing mill of rolled sheet |
Melting process | EF+LF+VD |
Production process |
Forging+heat treatment+rough machining+QT |
Forging ratio |
≥3.5 |
Applicable standard | ASTM,ASME,DIN,JIS,ISO,BS,API,EN |
Executive standard |
JB/GB/EN/DIN/JIS/ASME/ASTM/ISO |
Certification authority |
ISO9001:2008,BV,SGS, IST, UL,CTI |
Delivery term |
Rough machining(N+T);finish machining(Q+T) |
Test equipment |
Spectrograph,ut device,tensile and compact test machine,metalloscope,outside micrometer,bore dial indicator,hardness test machine |
Service | Our service included the forging, process, heat treatment, finish machining, package, local logistics, customers clearance and maritime transport. We took the customer’s requirements as the principal thing, and pay attention on the products quality. |
Custom properties
Material elements | C | Si | Mn | P | S | Cr | Ni | Mo |
Others |
4140 | 0.38-0.43 | 0.15-0.35 | 0.60-0.90 | ≤0.035 | ≤0.040 | 0.80-1.10 | -- | 0.15-0.25 | - |
60CrMo | 0.55-0.65 | 0.17-0.30 | 0.450-0.80 | ≤0.020 | ≤0.015 | 0.50-0.80 | ≤0.25 | 0.20-0.40 | |
9Cr2Mo | 0.85-0.95 | 0.25-0.45 | 0.20-0.40 | ≤0.025 | ≤0.025 | 1.70-2.10 | ≤0.25 | 0.20-0.40 |
Mechanical property |
Dia.(mm) |
TS/Rm(Mpa) |
YS/Rp0.2(Mpa) |
EL/A5(%) |
RA/Z(%) |
Type Of notch |
Impact energy |
HBW |
4140 | Ø25 | 740~1000 | 450~850 | ≥12 | ≥25 | V | ≥40 | ≤250HBS |
Process procedure:
Forging process flow quality control: Raw material steel ingot into warehouse(test the chemical content) → Cutting→ Heating(Furnace temperture test) → Heat treatment after forging(Furnace temperture test) Discharge the furnace(blank inspection)→ Machining→ Inspection(UT,MT,Visal diamention, hardness)→ QT→ Inspection(UT, mechanical properties, hardness, grain size)→ Finish machining→ Inspection (dimension)→ Packing and Marking(steel stamp, mark)→ Storage Shipment
Commerce clause
MOQ | 1PC |
Max length | 10000MM |
Delivery time | 30-60 days |
Package | Wood pallet,steel frame |
Delivery term | FOB;CIF;CFR;DDU; |
Payment term | T/T,LC |
Type of shipping |
By ocean,air |
Keywords:
cold roller has advantages of solidification crack,impact resistance,wear resistance,the materials of cold roller as follows: 4140,60CrMo,9Cr2Mo,90Cr3,and other high Cr material