Material: | 4130 | Equipment: | 8T Hammer |
---|---|---|---|
Melting process: | EF+VAR | Forging ratio: | ≥4 |
Heating treatment: | N+T Q+T | Weight: | 5 T |
Làm nổi bật: | forging stainless steel,super steel forgings |
Surface casing head 4130 casing head,alloy steel casing head
Reference:
Material | 4130 |
Equipment | 8T Hammer |
Application |
Surface casing head is the key connection parts between casing and well head |
Melting process |
EF+VAR |
Production process |
Forging-heat treatment after forging-rough machining-QT-finish machining-packing |
Forging ratio | ≥4 |
Applicable standard |
ASTM,ASME,DIN,JIS,ISO,BS,API,EN |
Executive standard |
JB/GB/EN/DIN/JIS/ASME/ASTM/ISO |
Certification authority |
ISO9001,PED (TÜV) |
Delivery term |
Each product is qualified,no material and machining defect,completely meet the mechanical property. |
Test equipment |
Spectrograph,UT,MT device,tensile and impact test machine,metalloscope,outside micrometer,bore dial indicator,hardness test machine |
Service |
Our service included the forging, process, heat treatment, finish machining, package, local logistics, customers clearance and maritime transport. We took the customer’s requirements as the principal thing, and pay attention on the products quality. |
Customs properties:
Material elements |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Cu |
V |
4130 | 0.28-0.33 | 0.15-0.35 | 0.4-0.7 | <0.025 | <0.025 | 0.8-1.0 | <0.5 | 0.15-0.25 | / |
<0.1 |
Mechanical property |
Dia.(mm) |
TS/Rm(Mpa) |
YS/Rp0.2(Mpa) |
EL/A5(%) |
RA/Z(%) |
Notch |
Impact energy |
HBW |
4130 | Ф10 | >655 | >517 | >18 | >35 | V | ≥20J(-60℃) | 197-237 |
Commerce clause:
Max weight | 5 T |
MOQ | 1PC |
Delivery date | 30-50 Days |
Package | Wooden case |
Delivery term | FOB;CIF |
Payment term | T/T,LC |
Transportation | Vehicle,ocean,air |
Keywords:
Surface casing head is the key connection parts between casing and well head ,the common material is 4130,The bottom end is connected with surface casing by screw,top end is connected with well head equipment by flange or clamp.
Procedure:
Forging process flow quality control: Raw material steel ingot into warehouse(test the chemical content) → Cutting→ Heating(Furnace temperture test) → Heat treatment after forging(Furnace temperture test) Discharge the furnace(blank inspection)→ Machining→ Inspection(UT,MT,Visal diamention, hardness)→ QT→ Inspection(UT, mechanical properties, hardness, grain size)→ Finish machining→ Inspection (dimension)→ Packing and Marking(steel stamp, mark)→ Storage Shipment