Thông tin chi tiết sản phẩm:
Thanh toán:
|
| Material: | Steel | Forging ratio: | ≥5 |
|---|---|---|---|
| Melting process: | EF+LF+VD | Application: | Wind power equipment |
| Heat treatment: | N+T | Size: | As drawing |
| Điểm nổi bật: | turbine rotor forging,turbine main shaft |
||
Q345E Turbine Rotor Forging Steam Turbine Shaft Wind Power Generation Door Frame
Products:
wind power door frame,wind power tower door frame,wind power equipment parts
Products reference:
| Material | Q345E |
| Max dia | 5000mm |
| Application |
Wind power equipment forging parts |
| Melting process | EF+LF+VD |
| Production process |
Hot rolled plate-Nomalizing-cutting-sample taking-UT-Mechanical property test-machining |
| Forging ratio |
/ |
| Applicable standard | ASTM,ASME,DIN,JIS,ISO,BS,API,EN ,DIN |
| Executive standard | JB/GB/EN/DIN/JIS/ASME/ASTM/ISO |
| Certification authority | ISO,BV,SGS, IST, UL,CTI |
| Delivery term |
finish machining |
|
Test equipment |
Spectrograph,UT device,tensile and compact test machine,metalloscope,outside micrometer,bore dial indicator,hardness test machine |
| Service |
Our service included the forging, process, heat treatment, finish machining, package, local logistics, customers clearance and maritime transport. We took the customer’s requirements as the principal thing, and pay attention on the products quality. |
Custom properties
| Material elements | C | Si | Mn | P | S | Cr | Ni | Mo | Cu |
| 4130 | 0.26-0.33 | 0.15-0.35 | 0.40-0.60 | ≤0.035 | ≤0.040 | 0.80-1.10 | ≤0.030 | 0.15-0.25 | ≤0.030 |
| Q345E | 0.13-0.20 | 0.17-0.37 | 1.20-1.60 | ≤0.030 | ≤0.030 | ≤0.30 | ≤0.30 | -- | |
| 18CrNiMo7-6 | 0.15-0.21 | 0.17-0.35 | 0.50-0.90 | ≤0.025 | ≤0.025 | 1.50-1.80 | 1.40-1.70 | 0.25-0.35 |
|
Mechanicl property |
Dia.(mm) |
TS/Rm(Mpa) |
YS/Rp0.2(Mpa) |
EL/A5(%) |
RA/Z(%) |
Type Of notch |
Impact energy |
HBW |
| 4130 | Ø25 | ≥930 | ≥785 | ≥12 | ≥50 | V | ≥63 | ≤229HBS |
| Q345E | Ø10 | 470-630 | ≥345 | ≥21 | -- | V | -20℃≥27 | ＝＝ |
| 18CrNiMo7-6 | Ø15 | ≥980 | ≥785 | ≥9 | ≥40 | V | ≥47 | ≤269HBS |
Process procedure:
Forging process flow quality control: Raw material steel ingot into warehouse(test the chemical content) → Cutting→ Heating(Furnace temperture test) → Heat treatment after forging(Furnace temperture test) Discharge the furnace(blank inspection)→ Machining→ Inspection(UT,MT,Visal diamention, hardness)→ QT→ Inspection(UT, mechanical properties, hardness, grain size)→ Finish machining→ Inspection (dimension)→ Packing and Marking(steel stamp, mark)→ Storage Shipment
Commerce clause
| Max weight | 30T |
| MOQ | 1PC |
| Delivery time | 15-50 days |
| Package | Plywood case,wood pallet,steel frame |
| Delivery term | FOB;CIF;CFR；DDU； |
| Payment | T/T,LC |
| Type of shipping |
By ocean,air |
Keywords
Wind power flange,main shaft locknut,annular gear,outer gear ring,slewing bearing,top flange,middle flange,bottom flange,flange disc
Note:
Người liên hệ: Mr. Arnold
Tel: +86-15-15-15-81-878
Fax: 86-512-58360318
| Văn phòng bán hàng:A 509,HuaJian Mansion,Zhangjiagang City,JiangSu Province,China | |
| +86--13914905080 | |
| arnoldxue@163.com | |